Horse Epoxy Anchoring
Type: HM-500
Volume: 390ml
Mix Ratio: 3:1
Color: Red or Black
Density: 1.5±0.1g/cm³
Packing: 30 cartridges/carton
Easy extrusion mixing, faster injection speed, higher construction effiency
The modification of epoxy resin not only keeps the synthetic superiority of collied,
but also shortens the curing time at low temperature.
High thixotropy, high strength, easy extrusion mixing, faster injection speed, higher construction efficiency.
Advanced nano material technology multi-dimensional mesh structure, good thixotropy. NO sagging for both side surface or top surface construction
HM-500 concrete injectable anchoring adhesive performance parameters | |
Appearance | A(main agent): white paste |
B(curing agent): red or black paste | |
Viscosity of mixture | 18~22 Pa·s |
Density of curing material | 1.50±0.10g/cm3 |
Mixture ratio (volume ratio) | 3:1 |
Storage period | 12 months |
Packageing | 390ml |
Operable time and curing time | |||||
Ambient temperature(℃) | -5 | 0 | 10 | 20 | ≥30 |
Operable time(℃) | 60 | 45 | 30 | 25 | 20 |
Curing time(h) | 72 | 48 | 24 | 12 | 6 |
HM-500 concrete injectable anchoring adhesive performance indexes | ||||
item | index | item | index | |
Colloidal performance | Splitting tensile strength(MPa) | ≥8.5 | Thixotropic index | ≥4.0 |
Bending strength(MPa) | ≥50 | Sagging mobility | ≤2.0mm | |
Compressive strength(MPa) | ≥60 | Distortion temperature | ≥65℃ | |
Adhesion performance | Steel-steel (steel sleeve) tensile anti-shear strength(MPa) | ≥10 | ||
Under the constraint drawing condition, ribbed steel bars and C30, φ25, L=150mm(MPa) | ≥11 | |||
Adhesion strength of concrete C60, φ25, L=125mm(MPa) | ≥17 | |||
Steel-steel T impact stripping length | ≤25mm | |||
Non-volatile matter content(solid content)(%) | ≥99 |